A 276 308 Enquiry | Print this page
SAE A 276 308 Details
SAE A 276 308 Standard Download
Category | Type | Grade | Microstructure | Designations |
---|---|---|---|---|
Grades | Stainless Steels | A 276 308 | Austenite | USA - SAE , A 276 (2010) - Stainless Steel Bars and Shapes |
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | - | 0.08 | ||
Si | - | 1.00 | ||
Mn | - | 2.00 | ||
P | - | 0.045 | ||
S | - | 0.03 | ||
Cr | 19.0 | 21.0 | ||
Ni | 10.0 | 12.0 |
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
454 (≥) | 791 (≥) | 22 | 13 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 213 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
248 (≥) | 847 (≥) | 23 | 22 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 311 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
743 | 691 | 271 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
308 | UNS | USA | Chemical compositions of SAE wrought stainless steels |
308 | UNS | USA | Chemical compositions, mechanical and physical properties of SAE aluminum casting alloys |
A 167 Type 308 | SAE | USA | Stainless and Heat-Resisting Chromium-Nickel Steel Plate, Sheet, and Strip |
A 276 308 | SAE | USA | Stainless Steel Bars and Shapes |
A 314 308 | SAE | USA | Stainless Steel Billets and Bars for Forging |
A 473 308 | SAE | USA | Stainless Steel Forgings |
A 580 Type 308 | SAE | USA | Stainless Steel Wire |
A 959 Type 308 | SAE | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
A 167 S30800 | SAE | USA | Stainless and Heat-Resisting Chromium-Nickel Steel Plate, Sheet, and Strip |
A 276 S30800 | SAE | USA | Stainless Steel Bars and Shapes |
A 314 S30800 | SAE | USA | Stainless Steel Billets and Bars for Forging |
A 473 S30800 | SAE | USA | Stainless Steel Forgings |
A 580 S30800 | SAE | USA | Stainless Steel Wire |
S30800 | SAE | USA | Austenitic Chromium Nickel Heat Resisting Steel |
308L | AMS | USA | Bare Stainless Steel Welding Electrodes and Rods |
ER 308L | International | USA | Austenitic wire for metal inert gas welding. It is suitable for welding corrosion resistant 18/8 CrNi steels for devices, vessels and parts in chemical, pharmacy and cellulose industry for temperature up to 350°C. Welded material has oxidation resistance |
S30803 | AISI | USA | Austenitic wire for metal inert gas welding. It is suitable for welding corrosion resistant 18/8 CrNi steels for devices, vessels and parts in chemical, pharmacy and cellulose industry for temperature up to 350°C. Welded material has oxidation resistance |
A 167 S30815 | SAE | USA | Stainless and Heat-Resisting Chromium-Nickel Steel Plate, Sheet, and Strip |
A 213 S30815 | SAE | USA | Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
A 240 S30815 | SAE | USA | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |