Home»Products > Tool Die Steels > D2(Cr12Mo1V1) Hot Rolled Plate

D2(Cr12Mo1V1) Hot Rolled Plate

Quick Details

D2(Cr12Mo1V1) Hot Rolled Plate, ASTM A 681 Wrought alloy tool steel products

Delivery

  • Delivery status:Hot-Rolled 、Q+T 、Annealed 、
  • Surface:Blank 、Milling 、Pickled 、
  • Standard:ASTM
  • Shape:Round,Flat,Square,Hexagon,Plate,Sheet,Other

Inventory Status

View Inventory

D2(Cr12Mo1V1) Hot Rolled PlateRange of products
Product typeProductsDimensionProcesses
Plates/SheetsPlates/Sheets0.08-200mm(T)*W*LForging,hot rolling and cold rolling
Steel BarRound Bar,Flat Bar,Square BarΦ8-1200mm*LForging,hot rolling and cold rolling,Cast
Coil/StripSteel Coil/Steel Strip0.03-16.0x1200mmCold-Rolled&Hot-Rolled
Pipes/TubesSeamless Pipes/Tubes,Welded Pipes/TubesOD:6-219mm x WT:0.5-20.0mmHot extrusion,Cold Drawn,Welded

View chemical composition and mechanical properties of D2(Cr12Mo1V1) Hot Rolled Plate(D2(Cr12Mo1V1) Hot Rolled Plate Datasheet and Material certificate)

Product Details

D2(Cr12Mo1V1) Hot Rolled Plate

Hardness

  • Bar, wire, sheet; Annealed < 255 HB
  • Bar, wire, sheet; Cold drawn < 269 HB
  • Bar, wire, sheet; Heat treated > 59 HRC

Chemical Composition [%]

C 1.4000 1.6000 -
Si 0.1000 0.6000 -
Mn 0.1000 0.6000 -
P - 0.0300 -
S - 0.0300 -
Cr 11.000 13.000 -
Mo 0.7000 1.2000 -
V 0.5000 1.1000 -
Ni+Cu - 0.7500 


Heat Treatment

Preheat to 815 +/- 4℃, austenitize at either 996 +/- 12℃ in a salt bath or 1010 +/- 12℃ in a controlled atmosphere furnace for 10 to 20 minutes.
Quench in air then temper at 200℃ for 2 hours.
 

Cross Reference Table

 