ГОСТ у8гA-1Enquiry|Print this page

у8гA-1Application:Carbide for cutting tools
CategoryTypeSteel gradeStandardCountry
Grades Special Alloy у8гA-1ГОСТRussia

Chemical composition%of the ladle analysis of gradeу8гA-1

C(％)Si(％)Mn(％)P(％)S(％)Cr(％)Ni(％)Cu(%)
0.80-0.900.17-0.330.33-0.58≤0.025≤0.018≤0.20≤0.250.25
Mechanical properties of gradeу8гA-1
Proof strength
Rp0.2(MPa)		Tensile strength
Rm(MPa)		Impact energy
KV(J)		Elongation at fracture
A(%)		Reduction in cross section on fracture
Z(%)		As-Heat-Treated ConditionBrinell hardness(HBW)
158(≥)323(≥)444341Solution and Aging,Annealing,Ausaging,Q+T,etc112
Physical properties of gradeу8гA-1
PropertyDensity
kg/dm3		Temperature T
°C/F		Specific heat
J/kgK		Thermal conductivity
W/mK		Electric resistance
µΩ·cm		Modulus of elasticity
kN/mm2		Expansion rate
491(≥)219(≥)321332Solution and Aging,Annealing,Ausaging,Q+T,etc111
Temp.
°C/°F		Creep strain limit
(10000h)
(Rp1,0)N/mm2		Creep rupture strength
(10000h)
(Rp1,0)N/mm2
954183944
у8гA-1Range of products
Product typeProductsDimensionProcessesDeliver Status
Plates/SheetsPlates/Sheets0.08-200mm(T)*W*LForging,hot rolling and cold rollingAnnealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Steel BarRound Bar,Flat Bar,Square BarΦ8-1200mm*LForging,hot rolling and cold rolling,CastBlack,Rough Turning,Shot Blasting,
Coil/StripSteel Coil/Steel Strip0.03-16.0x1200mmCold-Rolled&Hot-RolledAnnealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Pipes/TubesSeamless Pipes/Tubes,Welded Pipes/TubesOD:6-219mm x WT:0.5-20.0mmHot extrusion,Cold Drawn,WeldedAnnealed,Solution and Aging,Q+T,ACID-WASHED
Cross Reference Table(Equivalent Grade)
GradeStandardCountryApplication
Y1Cr18Ni9ГОСТRussia
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9ГОСТRussia
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3NГОСТRussia
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
Y1Cr18Ni9SeГОСТRussia
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9ГОСТRussia
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Mn8Ni5NГОСТRussia
Nickel steel, instead of 1cr18ni9
00Cr18Ni10NГОСТRussia
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12ГОСТRussia
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
1Cr18Ni12Mo2TiГОСТRussia
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2TiГОСТRussia
Seamless stainless steel tubes for boiler and heat exchanger
G1800ГОСТRussia
Used in the products of the automobile, truck, tractor, and allied industries. Miscellaneous soft iron castings (as cast or annealed) in which strength is not of primary consideration. Exhaust manifolds may be made of this grade of iron, alloyed or unallo
F10008ГОСТRussia
Used in the products of the automobile, truck, tractor, and allied industries. Diesel engine castings, liners, cylinders, and pistons.
W108 CommerialГОСТRussia
Water quenching tool steel
00Cr17Ni14Mo2ГОСТRussia
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)
X2CrNiMo18-14-3ГОСТRussia
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)
1.4435ГОСТRussia
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)
Z 3 CND 17-11-02ГОСТRussia
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)
TS 60ГОСТRussia
Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)
0Cr18Ni12Mo2Cu2ГОСТRussia
0Cr18Ni12Mo2Cu2 stainless steel corrosion resistance, resistance to corrosion resistance is better than 0Cr17Ni12Mo2. 0Cr18Ni12Mo2Cu2 stainless steel used in the sulphuric acid resistant material.
00Cr18Ni14Mo2Cu2ГОСТRussia
00Cr18Ni14Mo2Cu2 0Cr18Ni12Mo2Cu ultra-low carbon steel, stainless steel 00Cr18Ni14Mo2Cu2 stainless steel is better than 0Cr18Ni12Mo2Cu2 resistance to intergranular corrosion.

Relevant products

у8гA-1 Steel Stock

Steel gradeDimensionShapeUnitQuantityDelivery stateQuery
Cr8 flat bar12*355*LFlat or Square barKgs3965Forged+Annealed+blackEnquiry
IncoloyA-286 / GH 2132 StockΦ8-65mm*LRound BarKgs489Hot-Rolled+Annealed+blackEnquiry
Incoloy800 round barΦ115*1400Round BarKgs169Hot-Rolled+Annealed+blackEnquiry
1.2083 Forged PlateT:105-185mm*W:510*LPlate or SheetTons26Forged+QTEnquiry
1.4882 strip/sheet/plate stock3.5x200x1000-2000mmCoil or StripKgs200Cold-Rolled+AnnealedEnquiry
A387 F5 & Grade 5 sheet Coil strip0.5mmx200mmxCCoil or StripTons3Cold-Rolled+AnnealedEnquiry
A387 F5 & Grade 5 Hot Coil stockSelectTons3Hot-Rolled+Annealed+blackEnquiry
PH13-8Mo ForgingsSelect0SelectEnquiry
0Cr13Ni8Mo2Al, PH13-8Mo, 13-8Mo, XM-13 round bar stockSelect0SelectEnquiry

Enquiry