DIN X5CrNiCuNb16-4Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | X5CrNiCuNb16-4 | DIN | Germany |
Chemical composition%of the ladle analysis of gradeX5CrNiCuNb16-4
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) | Nb(%) |
|---|---|---|---|---|---|---|---|---|
| Max 0.07 | Max 0.70 | Max 1.50 | Max 0.040 | Max 0.015② | 15.0-17.0 | 3.00-5.00 | 3.00-5.00 | 5×C％Max 0.45 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 536(≥) | 242(≥) | 32 | 32 | 34 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 443 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 134(≥) | 937(≥) | 23 | 22 | 33 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 241 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 367 | 485 | 946 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X5CrNiCuNb16-4 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| 1.4542 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| X5CrNiCuNb16-4 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| 1.4542 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| X5CrNiCuNb16-4 | DIN | Germany | Stainless steels - Chemical composition |
| 17-4PH, 1.4542, X5CrNiCuNb16-4 | DIN | Germany | Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) |