ISO ISO 19Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | ISO 19 | ISO | ISO |
Chemical composition%of the ladle analysis of gradeISO 19
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | N(%) |
|---|---|---|---|---|---|---|---|---|
| Max 0.030 | Max 1.00 | Max 2.00 | Max 0.045 | Max 0.030 | 16.0-18.0 | 10.0-13.0 | 2.00-3.00 | Max 0.11 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 298(≥) | 581(≥) | 11 | 12 | 14 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 423 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 196(≥) | 831(≥) | 42 | 44 | 12 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 431 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 656 | 343 | 622 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 00Cr19Ni10 | ISO | ISO | Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts |
| 0Cr19Ni9N | ISO | ISO | Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components |
| 0Cr19Ni10NbN | ISO | ISO | Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES |
| 0Cr19Ni13Mo3 | ISO | ISO | Seamless stainless steel tubes for boiler and heat exchanger |
| 00Cr19Ni13Mo3 | ISO | ISO | Seamless stainless steel tubes for boiler and heat exchanger |
| 1Cr19A13 | ISO | ISO | Heat-resisting steel sheets and plates |
| XM-19 | ISO | ISO | Chemical compositions of SAE wrought stainless steels |
| A 269 S21900 | ISO | ISO | Seamless and Welded Austenitic Stainless Steel Tubing for General Service |
| A 276 S21900 | ISO | ISO | Stainless Steel Bars and Shapes |
| A 314 S21900 | ISO | ISO | Seamless and Welded Austenitic Stainless Steel Tubing for General Service |
| A 473 S21900 | ISO | ISO | Stainless Steel Forgings |
| A 580 S21900 | ISO | ISO | Stainless Steel Wire |
| A 580 S21900 | ISO | ISO | Stainless Steel Wire |
| A 813 S21900 | ISO | ISO | Stainless Steel Wire |
| S21900 | ISO | ISO | Austenitic Chromium Manganese Nickel Stainless Steel |
| SA-813 S21900 | ISO | ISO | Specification for Single- or Double-Welded Austenitic Stainless Steel Pipe |
| SA-814 S21900 | ISO | ISO | Specification for Cold-Worked Welded Austenitic Stainless Steel Pipe |
| A 240 S21904 | ISO | ISO | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| A 269 S21904 | ISO | ISO | Seamless and Welded Austenitic Stainless Steel Tubing for General Service |
| A 276 S21904 | ISO | ISO | Stainless Steel Bars and Shapes |