GBT 20CrMoEnquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | 20CrMo | GBT | China |
Chemical composition%of the ladle analysis of grade20CrMo
| C(％) | Si(％) | Mn(％) | Cr(％) | Mo(％) |
|---|---|---|---|---|
| 0.17-0.24 | 0.17-0.37 | 0.40-0.70 | 0.80-1.10 | 0.15-0.25 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 489(≥) | 447(≥) | 22 | 11 | 12 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 234 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 561(≥) | 879(≥) | 24 | 32 | 13 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 434 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 186 | 171 | 474 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X20CrMo13 | GBT | China | Rolled, Wrought or Cast Stainless Steel Products for Medical Instruments |
| 1.4120 | GBT | China | Rolled, Wrought or Cast Stainless Steel Products for Medical Instruments |
| X20CrMoNiNbV11-1 | GBT | China | Wrought steels for use at elevated temperatures in engines |
| X12CrNiMoV12-3 | GBT | China | Wrought steels for use at elevated temperatures in engines |
: failed to open stream: No such file or directory in <b>/www/wwwroot/tool-die-steels.com/cms/libs/classes/image.class.php</b> on line <b>1616</b><br />
/products/images/2020/0302/20200302011801466.jpg)
: failed to open stream: No such file or directory in <b>/www/wwwroot/tool-die-steels.com/cms/libs/classes/image.class.php</b> on line <b>1616</b><br />
/products/images/2020/0302/20200302043247439.jpg)
: failed to open stream: No such file or directory in <b>/www/wwwroot/tool-die-steels.com/cms/libs/classes/image.class.php</b> on line <b>1616</b><br />
/products/images/2020/0521/20200521023037646.png)