ASTM 18Ni Maraging SteelEnquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | 18Ni Maraging Steel | ASTM | USA |
Chemical composition%of the ladle analysis of grade18Ni Maraging Steel
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | Cu(%) | Co(%) | Al(%) | Ti(%) | Other(%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.03 | 0.10 | 0.10 | 0.010 | 0.010 | 0.50 | 18.00-19.00 | 4.60-5.20 | 0.50 | 8.50-9.50 | 0.05-0.15 | 0.50 -0.80 | Fe Bal |
treatment characteristics.
Applications: Typical applications for maraging include missile and rocket motor cases, landing and takeoff gear, munitions,
aerospace, extrusion tooling, die casting, high performance shafting, gears and fasteners.
Material Melt Method: Maraging melt method is a VIM (Vacuum Induction Melt) + VAR (Vacuum Arc Remelt)
As Shipped Condition: Maraging is supplied in the annealed and descaled condition. The alloy is very tough, relatively soft (36
Rc Max.), therefore, readily machined and formed.
*Bar Tolerances: .250” - .499” .500” - .999” 1.000” – 3.625” 3.626” – 6.000” 6.001” – 8.000” 8.001” – 10.000”
-.000/+.005 -.000/+.010 -.000/+.031 -.000/+.047 -.000/+.063 -.000/+0.078
Minimum Properties after Aging:
Hardness ……………… 52 Rc Charpy V-notch ……… 12 ft/lbs. min Reduction of Area ……. 47%
Elongation ……………. 5.0% Yield Strength …………. 280 ksi Fracture Toughness ….. 60
Physical Properties:
Density………………………………… .289 lbs./cu. In
Average Coefficient of Thermal Expansion (70 – 900 F) ……………… 5.6 x 10 -6 in/in. F
Heat Treatment Aging Process: (Non Die Casting Applications)
Material is to be heat treated to 900 F +/- 10 holding at temperature for 6 hours then cooling at room air temperature. During the aging
treatment maraging shrinks uniformly and predictably on all dimensions .001 in/in
Heat Treatment Aging Process: (Die Casting Applications)
Following the rough machining of the die, anneal at 1500-1525 F for 1 hour per inch of thickness is recommended. After finish
machining , an aging heat treatment of 980-1000 F for 6 hours is recommended.
Machining:
Maraging steel in the annealed condition is comparable to 4340. However, when maraging is aged, the type of cutting tool and speeds
change. Rigid equipment, firm tool supports, sharp tools and abundant coolant are essential.
Welding:
Maraging is weld able without preheat, in both the annealed and aged condition. Only an aging heat treatment is needed to restore in the
weld.
Standards:
AMS 6514 ASTM A 538 *Mil-S-46850D UNS K93120
*DMI product is not supplied to the dimensional tolerances of MIL-S-46850D.
*The information, data and specifications presented here are representative only, and are not guaranteed values. Material or products
applications described are solely for illustrative purposes and should not be construed as express or implied warranties for fitness for these
or other applications
As Shipped Condition: Maraging is supplied in the annealed and descaled condition. The alloy is very tough, relatively soft (36
Rc Max.), therefore, readily machined and formed.
*Bar Tolerances: .250” - .499” .500” - .999” 1.000” – 3.625” 3.626” – 6.000” 6.001” – 8.000” 8.001” – 10.000”
-.000/+.005 -.000/+.010 -.000/+.031 -.000/+.047 -.000/+.063 -.000/+0.078
Minimum Properties after Aging:
Hardness ……………… 52 Rc Charpy V-notch ……… 12 ft/lbs. min Reduction of Area ……. 47%
Elongation ……………. 5.0% Yield Strength …………. 280 ksi Fracture Toughness ….. 60
Physical Properties:
Density………………………………… .289 lbs./cu. In
Average Coefficient of Thermal Expansion (70 – 900 F) ……………… 5.6 x 10 -6 in/in. F
Heat Treatment Aging Process: (Non Die Casting Applications)
Material is to be heat treated to 900 F +/- 10 holding at temperature for 6 hours then cooling at room air temperature. During the aging
treatment maraging shrinks uniformly and predictably on all dimensions .001 in/in
Heat Treatment Aging Process: (Die Casting Applications)
Following the rough machining of the die, anneal at 1500-1525 F for 1 hour per inch of thickness is recommended. After finish
machining , an aging heat treatment of 980-1000 F for 6 hours is recommended.
Machining:
Maraging steel in the annealed condition is comparable to 4340. However, when maraging is aged, the type of cutting tool and speeds
change. Rigid equipment, firm tool supports, sharp tools and abundant coolant are essential.
Welding:
Maraging is weld able without preheat, in both the annealed and aged condition. Only an aging heat treatment is needed to restore in the
weld.
Standards:
AMS 6514 ASTM A 538 *Mil-S-46850D UNS K93120
*DMI product is not supplied to the dimensional tolerances of MIL-S-46850D.
*The information, data and specifications presented here are representative only, and are not guaranteed values. Material or products
applications described are solely for illustrative purposes and should not be construed as express or implied warranties for fitness for these
or other applications
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 412(≥) | 456(≥) | 42 | 13 | 42 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 342 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 733(≥) | 747(≥) | 34 | 22 | 43 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 244 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 974 | 963 | 658 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| Y1Cr18Ni9 | ASTM | USA | Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut |
| 1Cr18Ni9 | ASTM | USA | High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts |
| Y1Cr18Ni9Se | ASTM | USA | Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws |
| 0Cr18Ni9 | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 00Cr18Ni10N | ASTM | USA | In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance |
| 1Cr18Ni12 | ASTM | USA | Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading |
| 1Cr18Ni12Mo2Ti | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr18Ni12Mo2Ti | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr18Ni12Mo2Cu2 | ASTM | USA | 0Cr18Ni12Mo2Cu2 stainless steel corrosion resistance, resistance to corrosion resistance is better than 0Cr17Ni12Mo2. 0Cr18Ni12Mo2Cu2 stainless steel used in the sulphuric acid resistant material. |
| 00Cr18Ni14Mo2Cu2 | ASTM | USA | 00Cr18Ni14Mo2Cu2 0Cr18Ni12Mo2Cu ultra-low carbon steel, stainless steel 00Cr18Ni14Mo2Cu2 stainless steel is better than 0Cr18Ni12Mo2Cu2 resistance to intergranular corrosion. |
| 1Cr18Ni12Mo3Ti | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr18Ni12Mo3Ti | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr18Ni16Mo5 | ASTM | USA | Stainless steel bars |
| 1Cr18Ni9Ti | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr18Ni10Ti | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 0Cr18Ni11Nb | ASTM | USA | Heavy stainless acid resistant and heat resistant steel forgings |
| 0Cr18Ni9Cu3 | ASTM | USA | Stainless steel bars |
| 0Cr18Ni13Si4 | ASTM | USA | Seamless stainless steel tubes for boiler and heat exchanger |
| 1Cr18Ni11SiA1Ti | ASTM | USA | Stainless steel bars |
| 00Cr18Ni5Mo3Si2 | ASTM | USA | Stainless steel bars |