AISI AISI 414Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | AISI 414 | AISI | USA |
Chemical composition%of the ladle analysis of gradeAISI 414
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) |
|---|---|---|---|---|---|---|
| 0.15 | 1.00 | 1.00 | 0.04 | 0.03 | 11.5-13.5 | 1.25-2.50 |
Steel is the common name for a large family of iron alloys. Steels can either be cast directly to shape, or into ingots which are reheated and hot worked into a wrought shape by forging, extrusion, rolling, or other processes. Wrought steels are the most common engineering material used, and come in a variety of forms with different finishes and properties. Stainless steels are high-alloy steels that have superior corrosion resistance than other steels because they contain large amounts of chromium. Stainless steels contains at least 10% chromium, with or without other elements. Stainless steels can be divided into three basic groups based on their crystalline structure: austenitic, ferritic, and martensitic.
The typical elastic modulus of stainless steels at room temperature (25°C) ranges from 190 to 210 GPa. The typical density of stainless steels ranges from 7.75 to 8.1 g/cm3. The typical tensile strength varies between 515 and 827 MPa. The wide range of ultimate tensile strength is largely due to different heat treatment conditions.
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 866(≥) | 127(≥) | 43 | 13 | 13 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 441 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 824(≥) | 395(≥) | 42 | 23 | 24 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 114 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 524 | 173 | 955 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH4141 | AISI | USA | Iron-based superalloy |
| GH4145 | AISI | USA | Nickel-base superalloy |
| GH4146 | AISI | USA | Nickel-base superalloy |
| A 276 S41400 | AISI | USA | Stainless Steel Bars and Shapes |
| A 314 S41400 | AISI | USA | Stainless Steel Billets and Bars for Forging |
| A 473 S41400 | AISI | USA | Stainless Steel Forgings |
| A 580 S41400 | AISI | USA | Stainless Steel Wire |
| S41400 | AISI | USA | Martensitic Chromium Stainless Steel |
| A 276 S41425 | AISI | USA | Stainless Steel Bars and Shapes |
| A 314 S41425 | AISI | USA | Stainless Steel Billets and Bars for Forging |
| A 473 S41425 | AISI | USA | Stainless Steel Forgings |
| A 479 S41425 | AISI | USA | Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels |
| A 565 S41425 | AISI | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| A 959 S41425 | AISI | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| S41425 | AISI | USA | Martensitic Chromium Nickel Molybdenum Nitrogen Stainless Steel |
| SA-479 S41425 | AISI | USA | Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels |
| NV7(4140) | AISI | USA | Steel for intake valves |
| H41400 | AISI | USA | Steel for intake valves |
| 1.2414 | AISI | USA | Alloyed W steel |