SAE H11 Details
SAE H11 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Tool Die Steels | H11 | USA - SAE , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.30 | 0.40 | ||
| Si | 0.80 | 1.20 | ||
| Mn | 0.20 | 0.40 | ||
| Cr | 4.75 | 5.50 | ||
| Mo | 1.25 | 1.75 | ||
| V | 0.30 | 0.50 | ||
| W | - | - |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 526 (≥) | 962 (≥) | 13 | 44 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 324 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 616 (≥) | 827 (≥) | 21 | 43 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 311 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 632 | 794 | 565 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH1131 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| GH1140 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| GH1138 | GB | China | Iron-based superalloy |
| GH1139 | GB | China | Iron-based superalloy |
| GH1167 | GB | China | Iron-based superalloy |
| SUH 11M | SAE | USA | Engine poppet valve information report |
| 03X18H11 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 06X18H11 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 08X16H11M3 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 08X16H11M3T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| SUH11 | CNS | China | CNS standard heat resistant steel bar steel grade and chemical composition |
| ISO H11 | ISO | International | Stainless steels - Chemical composition |
| H11 | ASTM | USA | Hot-Work Tool Steel |
| H11 | SAE | USA | Hot-Work Tool Steel |
| Incoloy 800 | UNS | USA | Equipment used in the manufacture of resistance to stress corrosion cracking |
| X19CrMoNbVN11-1,1.4913 | DIN | Germany | Heat Resisting and Highly Heat Resisting Materials for Bolts and Nuts; Quality Specifications |
Relevant products
H11 Steel Stock
| Steel grade | Dimension | Shape | Unit | Quantity | Delivery state | Query |
|---|---|---|---|---|---|---|
| Incoloy800 round bar | Φ115*1400 | Round Bar | Kgs | 169 | Hot-Rolled+Annealed+black | Enquiry |