SAE H20 Details
SAE H20 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Tool Die Steels | H20 | USA - SAE , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.25 | 0.35 | ||
| Si | 0.10 | 0.75 | ||
| Mn | 0.10 | 0.40 | ||
| Cr | 1.80 | 2.20 | ||
| Mo | - | - | ||
| V | 0.40 | 0.60 | ||
| W | 9.00 | 10.00 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 142 (≥) | 919 (≥) | 43 | 23 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 124 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 561 (≥) | 568 (≥) | 44 | 24 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 424 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 362 | 191 | 484 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH2018 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| GH2036 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| GH2038 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| 08X10H20T2 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 10X11H20T3P | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 20X25H20C2 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 07X17H20M2Д2T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 1OXl1H20T2P | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 10X12H20T2 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 10Xl1H20T2P(ЭИ696A) | GOST | Russia | Russia GOCT standard deformation of high temperature alloy grades and chemical composition |
| ISO H20 | ISO | International | Nickel and nickel alloy forgings |
| H20 | SAE | USA | Hot-Work Tool Steel |