A 965 S32109 Enquiry | Print this page
SAE A 965 S32109 Details
SAE A 965 S32109 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | A 965 S32109 | Austenite | USA - SAE , A 965/A 965M (2012) - Steel Forgings, Austenitic, for Pressure and High Temperature Parts |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.04 | 0.10 | ||
| Mn | - | 2.00 | ||
| Si | - | 1.00 | ||
| P | - | 0.04 | ||
| S | - | 0.03 | ||
| Cr | 17.00 | 20.00 | ||
| Ni | 9.00 | 12.00 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 626 (≥) | 296 (≥) | 11 | 42 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 433 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 154 (≥) | 388 (≥) | 12 | 31 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 166 | 322 | 156 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 240 S32109 | SAE | USA | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| A 249 S32109 | SAE | USA | Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes |
| A 358 S32109 | SAE | USA | Electric-Fusion-Welded Austenitic Chromium-Nickel Stainless Steel Pipe for High-Temperature Service and General Applications |
| A 813 S32109 | SAE | USA | Single- or Double-Welded Austenitic Stainless Steel Pipe |
| A 814 S32109 | SAE | USA | Cold-Worked Welded Austenitic Stainless Steel Pipe |
| A 965 S32109 | SAE | USA | Steel Forgings, Austenitic, for Pressure and High Temperature Parts |
| S32109 | AISI | USA | Austenitic Chromium Nickel Stainless Steel (Titanium Stabilized, High carbon) |
| SA-240 S32109 | AMS | USA | Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| SA-403 S32109 | AMS | USA | Specification for Wrought Austenitic Stainless Steel Piping Fittings |
| SA-813 S32109 | AMS | USA | Specification for Single- or Double-Welded Austenitic Stainless Steel Pipe |
| SA-814 S32109 | AMS | USA | Specification for Cold-Worked Welded Austenitic Stainless Steel Pipe |
| SA-965 S32109 | AMS | USA | Specification for Steel Forgings, Austenitic, for Pressure and High Temperature Parts |
| SUS 321HFB | JIS | Japan | Stainless steel blooms and billets for forgings |
| SUS 321HTP | JIS | Japan | Stainless steel pipes |
| STSF321H | KS | Korea | Stainless steel forgings for pressure vessels |