UNS HP 9-4-25 Details
UNS HP 9-4-25 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | HP 9-4-25 | Precipitation-Hardening | USA - UNS , SAE AMS 6546F - Steel Sheet, Strip, and Plate 0,48Cr - 8,0Ni - 4,0Co - 4,48Mo - 0,09V - (0,24 - 0,30C) Consumable Electrode Melted, Annealed |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.24 | 0.30 | ||
| Si | - | 0.10 | ||
| Mn | 0.10 | 0.35 | ||
| Ni | 7.00 | 9.00 | ||
| Cr | 0.35 | 0.60 | ||
| Al | - | - | ||
| Cu | - | - | ||
| Ti | - | - | ||
| Fe | - | - | ||
| Mo | 0.35 | 0.60 | ||
| Co | 3.50 | 4.50 | ||
| V | 0.06 | 0.12 | ||
| P | - | 0.01 | ||
| S | - | 0.01 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 325 (≥) | 158 (≥) | 42 | 41 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 313 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 222 (≥) | 271 (≥) | 21 | 24 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 315 | 344 | 582 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 646 Grade HP 9-4-20 | SAE | USA | Premium Quality Alloy Steel Blooms and Billets for Aircraft and Aerospace Forgings |
| HP 9-4-20 | ASTM | USA | Steel, Sheet, Strip, and Plate 0.75Cr - 9.0Ni - 4.5Co - 1.0Mo - 0.09V (0.17 - 0.23C) Vacuum Consumable Electrode Melted, Annealed |
| HP 9-4-20 | ASTM | USA | Steel, Bars, Forgings, Tubing, and Rings 0.75Cr - 9.0Ni - 4.5Co - 1.0Mo - 0.09V (0.17 - 0.23C) Consumable Electrode Vacuum Melted |
| HP 9-4-20 | UNS | USA | Steel, Sheet, Strip, and Plate 0.75Cr - 9.0Ni - 4.5Co - 1.0Mo - 0.09V (0.17 - 0.23C) Vacuum Consumable Electrode Melted, Annealed |
| HP 9-4-20 | AMS | USA | Steel, Bars, Forgings, Tubing, and Rings 0.75Cr - 9.0Ni - 4.5Co - 1.0Mo - 0.09V (0.17 - 0.23C) Consumable Electrode Vacuum Melted |
| HP 9-4-25 | ASTM | USA | Steel Sheet, Strip, and Plate 0,48Cr - 8,0Ni - 4,0Co - 4,48Mo - 0,09V - (0,24 - 0,30C) Consumable Electrode Melted, Annealed |
| HP 9-4-25 | UNS | USA | Steel Sheet, Strip, and Plate 0,48Cr - 8,0Ni - 4,0Co - 4,48Mo - 0,09V - (0,24 - 0,30C) Consumable Electrode Melted, Annealed |
| A 646 Grade HP 9-4-30 | SAE | USA | Premium Quality Alloy Steel Blooms and Billets for Aircraft and Aerospace Forgings |
| HP 9-4-30 | ASTM | USA | Steel, Sheet, Strip, and Plate 1.0Cr - 7.5Ni - 4.5Co - 1.0Mo - 0.09V (0.29 - 0.34C) Consumable Electrode Vacuum Melted, Annealed |
| HP 9-4-30 | ASTM | USA | Steel, Bars, Forgings, Tubing, and Rings 1.0Cr - 7.5Ni - 4.5Co - 1.0Mo - 0.09V (0.29 - 0.34C) Consumable Electrode Vacuum Remelted, Annealed |
| HP 9-4-30 | UNS | USA | Steel, Sheet, Strip, and Plate 1.0Cr - 7.5Ni - 4.5Co - 1.0Mo - 0.09V (0.29 - 0.34C) Consumable Electrode Vacuum Melted, Annealed |
| HP 9-4-30 | UNS | USA | Steel, Bars, Forgings, Tubing, and Rings 1.0Cr - 7.5Ni - 4.5Co - 1.0Mo - 0.09V (0.29 - 0.34C) Consumable Electrode Vacuum Remelted, Annealed |