DIN NiCr20TiEnquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | NiCr20Ti | DIN | Germany |
Chemical composition%of the ladle analysis of gradeNiCr20Ti
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) | Co(%) | B(%) | Al(%) | Ti(%) |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.80-0.15 | Max 1.00 | Max 1.00 | Max 0.020 | Max 0.015 | 18.0-21.0 | 18.0-21.0 | Max 0.50 | Max 5.0 | Max 0.006 | Max 0.30 | 0.20-0.60 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 464(≥) | 695(≥) | 41 | 14 | 24 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 444 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 883(≥) | 766(≥) | 11 | 12 | 23 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 433 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 813 | 481 | 477 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| NiCr20Ti | DIN | Germany | Heat resisting steels and nickel alloys |
| 2.4951 | DIN | Germany | Heat resisting steels and nickel alloys |
| NiCr20TiAI | DIN | Germany | Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties |
| NiCr20Ti | DIN | Germany | Nickel and nickel alloy forgings |
| NiCr20TiAl | DIN | Germany | Heat-treatable steels, alloy steels and free-cutting steels -- Part 15: Valve steels for internal combustion engines |
| NC20T, NiCr20Ti, N06075, 2.4951, NiCr20Ti | DIN | Germany | Nickel and nickel alloy forgings |