ГОСТ 8Χ3Enquiry|Print this page
Category | Type | Steel grade | Standard | Country |
---|---|---|---|---|
Grades | Special Alloy | 8Χ3 | ГОСТ | Russia |
Chemical composition%of the ladle analysis of grade8Χ3
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | V(%) | W(%) | Cu(%) | Ti(%) |
---|---|---|---|---|---|---|---|---|---|---|---|
0.75-0.85 | 0.15-0.35 | 0.15-0.40 | ≤0.030 | ≤0.030 | 3.20-3.80 | ≤0.35 | ≤0.20 | ≤0.15 | ≤0.20 | ≤0.30 | ≤0.03 |
Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
---|---|---|---|---|---|---|
883(≥) | 611(≥) | 23 | 33 | 43 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 132 |
Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
---|---|---|---|---|---|---|---|
488(≥) | 974(≥) | 43 | 24 | 33 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 331 | |
Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
691 | 617 | 771 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
Y1Cr18Ni9 | ГОСТ | Russia | Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut |
1Cr18Ni9 | ГОСТ | Russia | High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts |
1Cr18Mn10Ni5Mo3N | ГОСТ | Russia | Of urea with good corrosion resistance, can produce urea corrosion of the equipment. |
Y1Cr18Ni9Se | ГОСТ | Russia | Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws |
0Cr18Ni9 | ГОСТ | Russia | Seamless stainless steel tubes for boiler and heat exchanger |
1Cr18Mn8Ni5N | ГОСТ | Russia | Nickel steel, instead of 1cr18ni9 |
00Cr18Ni10N | ГОСТ | Russia | In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance |
1Cr18Ni12 | ГОСТ | Russia | Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading |
1Cr18Ni12Mo2Ti | ГОСТ | Russia | Seamless stainless steel tubes for boiler and heat exchanger |
0Cr18Ni12Mo2Ti | ГОСТ | Russia | Seamless stainless steel tubes for boiler and heat exchanger |
G1800 | ГОСТ | Russia | Used in the products of the automobile, truck, tractor, and allied industries. Miscellaneous soft iron castings (as cast or annealed) in which strength is not of primary consideration. Exhaust manifolds may be made of this grade of iron, alloyed or unallo |
F10008 | ГОСТ | Russia | Used in the products of the automobile, truck, tractor, and allied industries. Diesel engine castings, liners, cylinders, and pistons. |
W108 Commerial | ГОСТ | Russia | Water quenching tool steel |
00Cr17Ni14Mo2 | ГОСТ | Russia | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
X2CrNiMo18-14-3 | ГОСТ | Russia | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
1.4435 | ГОСТ | Russia | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
Z 3 CND 17-11-02 | ГОСТ | Russia | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
TS 60 | ГОСТ | Russia | Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007) |
0Cr18Ni12Mo2Cu2 | ГОСТ | Russia | 0Cr18Ni12Mo2Cu2 stainless steel corrosion resistance, resistance to corrosion resistance is better than 0Cr17Ni12Mo2. 0Cr18Ni12Mo2Cu2 stainless steel used in the sulphuric acid resistant material. |
00Cr18Ni14Mo2Cu2 | ГОСТ | Russia | 00Cr18Ni14Mo2Cu2 0Cr18Ni12Mo2Cu ultra-low carbon steel, stainless steel 00Cr18Ni14Mo2Cu2 stainless steel is better than 0Cr18Ni12Mo2Cu2 resistance to intergranular corrosion. |
Relevant products
A387 F5 / Grade 5 Coil / Sheet
1.4980 Round Bar
1.4980
GH 3536 Sheet
UNS NO7718 Coil/Strip/Sheet
Cr8 flat bar
IncoloyA-286 / GH 2132
S66286 round bar
Inconel718 round bar
NO8020 round bar
Incoloy800 round bar
Incoloy825 round bar
NO8825 round bar
Inconel825 round bar
Incoloy800 round bar
NO8020/No8031/N08367/NO8810/NO8825 Forging
GH 3536 Sheet
06Cr19Ni10/S30408/304/S30400/1.4301 Tube
S30409/304H/S30409/1.4948 Tube
S32168/321/S32100/1-4541 Tube
8Χ3 Steel Stock
Steel grade | Dimension | Shape | Unit | Quantity | Delivery state | Query |
---|---|---|---|---|---|---|
Cr8 flat bar | 12*355*L | Flat or Square bar | Kgs | 3965 | Forged+Annealed+black | Enquiry |
IncoloyA-286 / GH 2132 Stock | Φ8-65mm*L | Round Bar | Kgs | 489 | Hot-Rolled+Annealed+black | Enquiry |
Incoloy800 round bar | Φ115*1400 | Round Bar | Kgs | 169 | Hot-Rolled+Annealed+black | Enquiry |
1.2083 Forged Plate | T:105-185mm*W:510*L | Plate or Sheet | Tons | 26 | Forged+QT | Enquiry |
1.4882 strip/sheet/plate stock | 3.5x200x1000-2000mm | Coil or Strip | Kgs | 200 | Cold-Rolled+Annealed | Enquiry |
A387 F5 & Grade 5 sheet Coil strip | 0.5mmx200mmxC | Coil or Strip | Tons | 3 | Cold-Rolled+Annealed | Enquiry |
A387 F5 & Grade 5 Hot Coil stock | Select | Tons | 3 | Hot-Rolled+Annealed+black | Enquiry | |
PH13-8Mo Forgings | Select | 0 | Select | Enquiry | ||
0Cr13Ni8Mo2Al, PH13-8Mo, 13-8Mo, XM-13 round bar stock | Select | 0 | Select | Enquiry | ||
17-4PH Coil Stock | 0.08*200mm | Coil or Strip | Kgs | 1623 | Cold-Rolled+Annealed | Enquiry |
17-4PH Round Bar | Φ5-300mm*L | Round Bar | Kgs | 46958 | Hot-Rolled+Annealed+black | Enquiry |
17-4PH plate | 8-45*1200*3000mm | Plate or Sheet | Tons | 4.9 | Hot-Rolled+Annealed+black | Enquiry |
Cr12MoV | 12-160(T)*310-610(W)*L | Plate or Sheet | Tons | 12.38 | Hot-Rolled+Annealed+black | Enquiry |
1.2601 | 12-160(T)*310-610(W)*L | Plate or Sheet | Tons | 11.22 | Hot-Rolled+Annealed+black | Enquiry |
17-7PH / 631 Coil & Strip, Sheet Stock | 0.3-3.0*10-180mm | Coil or Strip | Kgs | 1236.22 | Cold-Rolled+Annealed | Enquiry |
X22CrMoV12-1 / 1.4923 | Φ17mm | Round Bar | Kgs | 300 | Hot-Rolled+Annealed+black | Enquiry |
X22CrMoV12-1 / 1.4923 | Φ30mm | Round Bar | Kgs | 300 | Hot-Rolled+Annealed+black | Enquiry |