H10 Enquiry | Print this page
ASTM H10 Details
ASTM H10 Standard Download
Category | Type | Grade | Designations |
---|---|---|---|
Grades | Tool Die Steels | H10 | USA - ASTM , |
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | 0.35 | 0.45 | ||
Si | 0.80 | 1.20 | ||
Mn | 0.25 | 0.70 | ||
P | - | 0.030 | ||
S | - | 0.030 | ||
Cr | 3.00 | 3.75 | ||
Mo | 2.00 | 3.00 | ||
V | 0.25 | 0.75 | ||
W | - | - | ||
Ni+Cu | - | 0.75 |
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
622 (≥) | 648 (≥) | 12 | 42 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 143 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
737 (≥) | 725 (≥) | 41 | 32 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
475 | 578 | 569 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
GH1015 | GB | China | Solid solution strengthening type iron base alloy |
GH1016 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
GH1035 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
GH1040 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
GH1013 | GB | China | Iron-based Superalloy |
GH1014 | GB | China | Iron-based superalloy |
04X18H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
08X18H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
08X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
12X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
12X18H10E | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
03X18H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
03X19Ar3H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
06X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
09X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
10X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
25X18H10B2 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
ISO H10 | ISO | International | Stainless steels - Chemical composition |
H10 | ASTM | USA | Hot-Work Tool Steel |
H10 | SAE | USA | Hot-Work Tool Steel |