H10 Enquiry | Print this page
SAE H10 Details
SAE H10 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Tool Die Steels | H10 | USA - SAE , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.40 | ||
| Si | 0.20 | 0.40 | ||
| Mn | 0.20 | 0.40 | ||
| Cr | - | 3.25 | ||
| Mo | - | 2.50 | ||
| V | - | 0.40 | ||
| W | - | - |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 883 (≥) | 256 (≥) | 13 | 32 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 221 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 997 (≥) | 868 (≥) | 12 | 41 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 841 | 566 | 597 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH1015 | GB | China | Solid solution strengthening type iron base alloy |
| GH1016 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| GH1035 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| GH1040 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |
| GH1013 | GB | China | Iron-based Superalloy |
| GH1014 | GB | China | Iron-based superalloy |
| 04X18H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 08X18H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 08X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 12X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 12X18H10E | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 03X18H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 03X19Ar3H10 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 06X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 09X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 10X18H10T | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 25X18H10B2 | GOST | Russia | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| ISO H10 | ISO | International | Stainless steels - Chemical composition |
| H10 | ASTM | USA | Hot-Work Tool Steel |
| H10 | SAE | USA | Hot-Work Tool Steel |